16001400• AQuestion1:O 1200a)Draw the microstructure at each of thepoints A, B, C, D in the phase diagramY. Austenito1000Dy+ Fe,Cgiven on the left.8000.76a - Fe;Cb)Clearly describe the characteristics offerrite, austenite, pearlite and cementite.600a, Ferrite4000.3.6.70FeComposition (wt% C)Cementite(Fe;C)Temperature ("C)

a) Iron carbon phase diagram from figure From the figure, it shows that at point A only the liquid…

Answered: a)Draw the microstructure at each of…

a)Draw the microstructure at each of the points A, B, C, D in the phase diagram given on the left. b)Clearly describe the characteristics of ferrite, austenite, pearlite and cementite.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: omenclature 2 composition, 3 crystal structure 4 Phase Diagrams,

A: Spheroidal graphite iron, also referred to as ductile cast iron, nodular cast iron, SG iron, and…

Q: Consider 2.4 kg of a 99.7 wt% Fe-0.3 wt% C alloy that is cooled to a temperature just below the…

Q: B) What is the difference between the Eutectic alloy and other alloy in the phase diagrams ? explain…

A: Eutectic alloy example: 4.3 % carbon cast iron 60% Sn- Pb-Sn alloy : solder

Q: For a 99.64 wt% Fe-0.36 wt% C steel at a temperature right below the eutectoid, a) the phase…

A: The weight % of carbon, The weight % of carbon at the eutectoid point, The weight % of ferrite,…

Q: Reproduce the binary phase diagram depicted in Fig. 3.20. For the composition shown at X, mark on…

A: Binary Phase diagrams: These are temperature vs composition diagrams in which two phases are…

Q: Sketch a phase diagram for two soluble components. Show the melting tem-perature of each element.…

A: The simplest type of phase diagram for any system can be of two components that are soluble in both…

Q: A 50 wt% Ni–50 wt% Cu alloy is slowly cooled from 1400°C (2550°F) to 1200°C (2190°F) (d) What is…

A: Solution: Given: A 50 wt% Ni–50 wt% Cu alloy is slowly cooled from 1400°C (2550°F) to 1200°C…

Q: What is the maximum amount of Pb (in %) with which Sn may be alloyed to render a single β phase at…

Q: One major difference with phase diagram is that there are three seperate phase. List out of solid…

A: given; One major difference with phase diagram is that there are three separate phase. List out of…

Q: Explain the differences between eutectic and eutectoid phase reactions.

A: The key difference between eutectic and eutectoid reaction is that in eutectic reactions, a liquid…

Q: On the phase diagram below indicate the range of wt% of carbon for steel, cast irons, and BCC-iron.

Q: (a) The Fe-C phase diagram is show in Figure Q5(a). Answer the following questions based on the…

A: Given: The mass fraction of pro eutectoid ferrite = 0.28 The mass fraction of pearlite = 0.72

Q: 4b) Figure 6 shows the Fe-Fe3C phase diagram. Evaluate (i) the temperature at which austenite…

Q: Q12. Carry out a phase analysis on the Bismuth-Cadmium eutectic composition.

A: Given question: Carry out a phase analysis on the Bismuth-Cadmium eutectic composition. The…

Q: Briefly explain the terms proeutectic, proeutectoid, and hypoeutectoid for the iron-iron carbide…

A: (A) Proeutectic phase – when we cool the liquid iron containing 4.3% carbon at 1147 0c,then it…

Q: ead-tin (Pb-Sn) is an eutectic type of phase diagram. At 183 °C, liquid (61.9 wt.% Sn), solid tin…

Q: b) Indicate corresponding cooling rates ( fast, mid-range, slow) and heat treatment c) Indicate a…

Q: Conducting the inverse lever rule on a phase diagram helps determine a) The amounts of phases b) The…

A: Conducting the inverse lever rule on a phase diagram helps determine the - The amounts of…

Q: An 80 wt% Cu - 20 wt% Ni alloy is slowly cooled from 1250 °C to 1100 °C. T(°C) 1600 L (liquid) 1500…

A: Given Composition: 80 wt% Cu and 20 wt %Ni Initial temperature = 1250 C Final temperature = 1100 C…

Q: Draw the iron-Fe3C phase diagram. Consider high carbon steel alloy.(min carbon content 0.9C%) a) It…

Q: Consider the hypothetical eutectic phase diagram for metals A and B, which is similar to that for…

A: Write the formula for the mass fraction of the primary β component of the given alloy.…

Q: Draw the iron carbon phase diagram and labeling all lines and areas. Then:- 1- find the melting…

A: Since you have posted a question with multiple sub-parts, we will solve first three sub parts for…

Q: a- Give the name for this type of phase diagram, and what is the main feature for this type? b-…

Q: Based on Figure 2, explain the importance of the L-S line in a hypothetical binary phase diagram for…

A: A phase diagram of an alloy is a graphical representation of all the phases present in the alloy…

Q: Suppose you wanted to have two samples of NiTi wire: one that is in the high-temperature austenite…

A: The high-temperature phase at 0 °C of the NiTi alloy is termed as Austenite. It tends to transform…

Q: The following questions are based on a high carbon steel with a composition of 1,5% C and 98,5% Fe.…

A: Given data:-105 w %C 98.5 w%FeC0=1.5 w%c

Q: For a 70-30 Zn-Cu alloy, what would the percent of each phase be at 800°C and 500°C?

A: Draw the phase diagram of Zn-Cu alloy as shown below –

Q: What are the effects of alloving elements on Fe-C binary phase diagram

A: The alloying element has strong effect on iron carbon phase diagram. for example when nickel and…

Q: Abul Khair (AKS) steel industry produced steel sample (austenite phase) which has 1.4% C for some…

A: As From the Iron -Carbon Diagram we had concluded that ***As per our company policy we are supposed…

Q: Construct the hypothetical phase diagram for metal A and B between temperature of 600 C° and 1000 C°…

A: according to the given question

Q: Temperature C For the phase diagram shown calculate the amount of austenite present at the point P…

A: For solution refer below images.

Q: Calculate the degrees of freedom for Points 1-4

A: Gibbs Phase rules - F= C-P+2 where F is the degrees of freedom C is number of components P is the…

Q: Consider 1.2 kg of a 99.6 wt% Fe-0.4 wt% C alloy that is cooled to a temperature just below the…

Q: 1)What is types of cast iron? Explain detail with; a)Elemental composition b)Production method…

A: 1 2

Q: What is the crystal structure of martensite? Why can you not find a martensite phase region in the…

A: The crystal structure of the martensite is Body-Centered Tetragonal (BCT). It is a Body-Centered…

Q: 11. What do you understand by the terms (i) static and (ii) dynamic methods for determination of…

A: In static method the alloy is held at a fixed temperature in the two phase field of solid and…

Q: Calculate the weight fraction for phases at point B? what are those phases? Is there any eutectic…

Q: water bath at the same temperature. Do you expect that the microstructure of both pieces will be the…

A: 1) The shown diagram shows T-T-T diagram of eutectoid sleek containing 0.8% carbon in steel it is…

Q: Draw Fe-C binary phase diagram and compute percentage of the phases in eutectoid steel.

Q: Compare the Cu-Ni binary phase diagram with the Al2O3-Cr2O3 binary phase diagram. Why are they so…

A: Binary diagrams are the diagram which consists of two components. In which both can be metals (Cu…

Q: Use the Lead-Tin (Pb-Sn) phase diagram below to answer the following questions: Place the following…

A: Given:

Q: Discuss the following transformation in TTT diagram at eutectoid composition with their…

A: TTT diagrams are the short form of time-temperature-transformation diagrams which are the plot of…

Q: Describe experimental procedure to obtain a binary isomorphic phase diagram for metals A and B by…

Q: What is the crystal phases just above eutectoid temperature for a carbon steel with carbon…

Q: In Figure 1 (phase diagram), an alloy composition of 95 wt% Mg and 5 wt% Al is cooled from 700 C to…

A: given data: alloy composition =95wt%Mg and 5wt%Alcooled from 700to 4750cε composition??

Q: What is meant by a phase? Describe an example. And what is the equilibrium phase diagram?

A: The phase of a substance is the region where the property of substance like density, index of…

Q: 1.9 kg of austenite containing 1.50 Wt% C is cooled from 1200 degrees C to a temperature just below…

A: Given: The mass of the austenite, m = 1.9 kg The wt% of C in austenite = 1.5% The temperature of…

Q: Material science Assuming this system forms a laminar type eutectic, determine the volume proportion…

Q: Question 1. (a) Why is the Fe-Fe,C phase diagram a metastable phase diagram instead of a true…

A: (a) In the Iron-Iron Carbide diagram, the Iron Carbide (Fe3C) is a unstable compound. It decomposes…

Q: different types of temperature-composition phase diagrams for an exemplary liquid-solid system

Question

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Iron carbon phase diagram

VIEW

Microstructure at point B

VIEW

Microstructure at point D:

VIEW

Ferrite and Austinite characterstics

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 4 steps with 5 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Phase Diagrams and Its Applications in Metallurgy

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Temperature C For the phase diagram shown calculate the amount of austenite present at the point P 1600 8+ liquid 1400 Liquid 1200 Fe,C+ liquid Y. 1000 y+Fe,C 800 a + Fe,C Fe,C- 600 2. 4. 6. C /wt%
3- The limited solid solubility Binary phase diagram has many types of reactions like and....... 4- the Crystal Structure of y (Austenite) is J. (12-1394) at 2.44 wt% has fec. 5- The maximum solubility of carbon in austenite, 2 occurs at 1147° C while the maximum solubility "wt% 0.022 W+% of BCC is At 727 oC ******* 6-steel alloys classified according to carbon conctration into.....n) and (hough). which are 7- in polymer structure the long molecules are composed of structural entities called repeat & Cham the along successively repeated and 8-polymer classified according to their molecular structure into hul (30Mark)
The figure below shows Pb-Sn phase diagram. What is the composition of Pb and Sn at point 1? 1200 1000 Liquid a +L 779 C (Tg) B+L 6 800 8.0 71.9 G 91.2 600 400 200 20 40 60 80 100 (Pb) Composition (wt% Sni (Sn) Callister Jr., W.D., 2007 O a. 80 wt % Sn and 20 wt % Pb O b. 10 wt % Sn and 90 wt % Pb O c. 90 wt % Sn and 10 wt % Pb O d. 20 wt % Sn and 80 wt % Pb Temperature ("C)
(c) in the Cu and Ag phase diagram shown in Figure 1.1, consider an alloy composition of 40 wt% Cu - 60 wt% Ag. Composton Ca RD 20 1200 우 100 2200 2000 1000 pnbn- :000 1600 8.0 1400 912 :200 G00 Sous :000 400 G00 200 0 400 100 40 60 Composition rwts AD Figure 1.1: Cu - Ag Phase Diagram i. What Phases are present in the Alloy at 800° C? i. What are the compositions of present phases if the alloy is cooled by 20° C? iii. What are the mass fraction of phases? If the alloy was further cooled by 2° C, determine the volume fraction of the phases? Take the densities of Cu and Ag as 8.96 and 10.49 g/cm' respectively. iv.
Q) Consider a 1.5 kg of a 99.7wt% Fe-0.3 wt% C alloy thatis cooled to a temperaturejust below the eutectoid.(a) How many kilograms of proeutectoid ferrite?(b) How many kilogram of cementite form ?(c) How many kilograms of all ferrite form? And How many kilograms of cutectoid ferrite?
b) Figure 2 is the tin-gold phase diagram, for which only single-phase regions are labeled. Write one (1) entectic point reaction and label all the non-label regions (i) - (viii). 1000 800 L (viii) Temperature (°C) 600 400 200 0 (Sn) (1) (v) B (vi) (iv) (ii) Y 8 20 40 60 80 Composition (wt% Au) Figure 2 Tin-gold phase diagram !(vii) T 100 (Au)
The following questions are based on a high carbon steel with a composition of 1,5% C and 98,5% Fe. Please refer to the Fe-Fe3C binary phase diagram in Callister and Rethwhich 1) a Name the phases present and calculate the amounts of these phases just above the eutectoid temperature b, Give the amount of austenite present at 1100°C. c. Give the amount of pro-eutectoid ferrite just above the eutectoid temperature. d. With equilibrium cooling just below the eutectoid temperature calculate the total ferrite. e. Why must the samples be quenched rapidly to obtain high hardness?
KS) A binary alloy having 28 wt% Cu and balance Ag solidifies at 779°C. The solid consists of two phases a and B. Phase a has 9% Cu whereas phase ß has 8 % Ag at 779°C. At room temperature these are pure Ag and Cu respectively Sketch the phase diagram. Label all phases and temperatures. The melting points of copper and silver are 1083° and 96100 respectively us? Estimate the amount of a and B in the above alloy at 779°C and at room temperature.) b) Calculate the mass fraction of phases for 40% Cu alloy at 300 °C and TR c) What is the composition of the alloys in (b) following:
1. Specify all temperature-compositicn points at which eutectics, eutectoids and peritectics. At 700 degrees Celsius and composition of 20% by weight of copper, calculate the compositions by fraction of each phase for copper? 1700 1500 L. 1300 1100 900 TiCu- 700 Ti:Cu4 500 20 40 60 (Ti) Composition (wt% Cu) to (0o) anjesedwa
Phase Diagrams: You are given the lead tin (Pb-Sn) phase diagram. Below the eutectic isotherm is identified as the two phase region a + B. a) At 30wt % Sn, in the circles below draw the microscopic observations evolving at 3000C, 2250C, and 1000C for this hypoeutectic alloy. b) At a temperature just above the isotherm at 1830C, for the 30 wt% Sn Alloy, calculate the fractions of each phase present at equilibrium and the corresponding composition of each phase.
For 40 wt% Sn – 60 wt% Pb alloy at 150 oC (at point B) as shown in Figure, i. State the name of phase(s) present. ii. Calculate the composition(s) of the phase(s) present. 600 300 Liquid 500 a+L 200 400 300 100 200 100 20 60 100 (Pb) (Sn) Composition (wt % Sn) Temperature ("C) Temperature ("F)
A binary alloy having 28 wt% Cu and balance Ag solidifies at 779°C. The solid consists of two phases a and B. Phase a has 9% Cu whereas phase ß has 8 % Ag at 779°C. At room temperature these are pure Ag and Cu respectively Sketch the phase diagram. Label all phases and temperatures. The melting points of copper and silver are 1083 and 9610 respectively s Pà) Estimate the amount of a and B in the above alloy at 779°C and at room temperature.) b) Calculate the mass fraction of phases for 40% Cu alloy at 300 °C and TR c) What is the composition of the alloys in (b)